POCAN® DP 7318 000000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KNWKqg_POCANDP7318000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 17 % white pigments, injection moulding, improved light reflection, low tendency to warp |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.50 | g/cm³ | ISO 1183 |
| Apparent Density | 0.90 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 27.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction : 260°C, 3.00mm 1 | 1.9 | % | ISO 2577 |
| Vertical flow direction : 110°C, 48 hours, 3.00mm 2 | 0.20 | % | ISO 294-4 |
| Flow direction : 260°C, 3.00mm 3 | 1.9 | % | ISO 2577 |
| Flow direction : 110°C, 48 hours, 3.00mm 4 | 0.20 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 94.0 | ml/g | ISO 1628 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 57.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 3200 | MPa | ISO 178/A |
| Flexural Stress 6(23°C) | 95.0 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength 7(23°C) | 6.0 | % |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT, GHMR, 09-030, MD17 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 130 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 110 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 160 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 190 | °C | ISO 306/B50 |
| Melting Temperature 8 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x3; MT 80°C; 600 Bar |
| 2 . | 150x150x3 |
| 3 . | 150x150x3; MT 80°C; 600 Bar |
| 4 . | 150x150x3 |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Pull Rate: 2 mm/min; 50% RH |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 FR | RTP Company | Nylon 66 | RTP |
| DuraFlex 781 | Evermore Chemical Industry Co., Ltd. | TPU-Polyester | DuraFlex |
| Dynaprene® VE0055A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Hylon® N7243HL | Ravago Manufacturing Americas, LLC | Nylon 6/12 | Hylon® |
| Latistat 62-08 | LATI S.p.A. | Nylon 6 | Latistat |