Durethan® BKV 40 H3.0 000000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS Corporation |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KMgx5I_DurethanBKV40H30000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % glass fibers, injection molding, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 280°C, 3.00mm 1 | 0.85 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 3.00mm 2 | 0.070 | -- | % | ISO 2577 |
| Flow direction : 280°C, 3.00mm 3 | 0.16 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 3.00mm 4 | 0.030 | -- | % | ISO 2577 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.0 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 12300 | 7800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 205 | 130 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 11000 | 7300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | -- | 180 | MPa | ISO 178/A |
| 23°C 6 | 325 | 205 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, MHR, 14-120, GF40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 18 | 24 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | 75 | kJ/m² | ISO 179/1eU |
| 23°C | 90 | 95 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 13 | 11 | kJ/m² | ISO 180/1A |
| 23°C | 18 | 24 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 6.00 | -- | J | ISO 6603-2 |
| 23°C | 9.00 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 200 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (23°C, 1.00 mm) | 40 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 23°C, 100 Hz | 4.00 | 15.0 | IEC 60250 | |
| 23°C, 1 MHz | 4.00 | 5.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 23°C, 100 Hz | 7.0E-3 | 0.20 | IEC 60250 | |
| 23°C, 1 MHz | 0.015 | 0.12 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index 9 | 24 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 150x105x3mm, 80°C MT, 400 bar |
| 2 . | 150x105x3mm |
| 3 . | 150x105x3mm, 80°C MT, 400 bar |
| 4 . | 150x105x3mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ASA S650 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| TECHNYL® A 218 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Kemcor HD 2470 | Qenos Pty Ltd | HDPE, HMW | Kemcor |
| INSPIRE™ TF2302 ESU | Trinseo | PP, Unspecified | INSPIRE™ |
| MAJORIS FG081 - 8487 | AD majoris | PP, Unspecified | MAJORIS |