LUVOCOM® 1100/GF/30/NAT Datasheet,PESU,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1100/GF/30/NAT is a polyethersulfone (PES) material, which contains a 30% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1100/GF/30/NAT are: flame retardant/rated flame sterilizable Good dimensional stability Typical application areas include: Electrical/electronic applications Reflector engineering/industrial accessories Aerospace Sporting goods

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	Good dimensional stability Good disinfection Hydrolysis resistance Disinfect with steam
Uses	Electrical/Electronic Applications Reflector Engineering accessories Aerospace applications Switch Sporting goods Medical/nursing supplies
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.59	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12000	MPa	ISO 527-2
Tensile Stress (Break)	140	MPa	ISO 527-2
Tensile Strain (Yield)	2.0	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	200	MPa	ISO 178
Flexural Strain at Flexural Strength	2.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	200	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	9.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	210	°C	ISO 75-2/A
Continuous Use Temperature	180	°C	UL 746B
CLTE - Flow	3.3E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.38	W/m/K	DIN 52612

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature - Desiccant Dryer	150	°C
Drying Time - Desiccant Dryer	3.0 - 5.0	hr
Suggested Max Moisture	0.050	%
Rear Temperature	355 - 375	°C
Middle Temperature	360 - 380	°C
Front Temperature	350 - 370	°C
Nozzle Temperature	340 - 360	°C
Processing (Melt) Temp	350	°C
Mold Temperature	120 - 200	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise porosity and surface defects (e.g. smearing) may occur. To avoid internal stresses, a low shear load should be used for processing. The parts may be tempered at a later stage to reduce internal stresses. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PESU , Polyethersulfone
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KMf0P0_LUVOCOM-1100-GF-30-NAT.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
NOVA PC 1023R	NOVA Polymers, Inc.	PC	NOVA PC
CarmelStat™ CS 1015	Carmel Olefins Ltd.	PP, Unspecified	CarmelStat™
Ferro PP TPP20AD76BK	Ferro Corporation	PP, Unspecified	Ferro PP
Eltex® P KS341	INEOS Olefins & Polymers Europe	PP Random Copolymer	Eltex® P
MAJORIS CE101E	AD majoris	Polyolefin, Unspecified	MAJORIS