Infino WP-1041G
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KLwGNQ_Infino-WP-1041G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WP-1041G is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/10.0 kg | 31 | g/10 min | |
| 250°C/2.16 kg | 3.0 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.50 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 105 | ASTM D785 | |
| R-Scale | 107 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 49.0 | MPa | ASTM D638 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Break 3 | 39.0 | MPa | ASTM D638 |
| Break | 41.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 100 | % | ASTM D638 |
| Break | 73 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1900 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 66.0 | MPa | ASTM D790 |
| -- 8 | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 47 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 390 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 250 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 540 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 410 | J/m | ASTM D256 |
| -30°C 10 | 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 120 | °C | ASTM D648 |
| 0.45 MPa, Annealed | 116 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Annealed, 4.00 mm | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 111 | °C | ISO 306/B50 |
| -- | 114 | °C | ISO 306/B120 |
| CLTE - Flow (40 to 100°C) | 8.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 78.5 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAFMER™ A-70090 | Mitsui Chemicals America, Inc. | PAO | TAFMER™ |
| DynaMix™ 5597 CFX | Polymer Dynamix | TP, Unspecified | DynaMix™ |
| Plasmer 1075B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |
| Sylvin 8200-70 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| LNP™ FARADEX™ NS003 compound | SABIC Innovative Plastics | PC+ABS | LNP™ FARADEX™ |