DOW™ VLDPE DFDB-1088 NT
| Category: | VLDPE , Very Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ VLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KLOdvf_DOW-VLDPE-DFDB-1088-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
DFDB-1088 NT Very Low Density Polyethylene (VLDPE) Resin is produced via gas phase polymerization from Dow. This is an ethylene-butene copolymer exhibiting high flexibility and elasticity. It can be utilized in monolayer and coextruded films and in blends with other polyolefins to enhance melt strength and toughness of the structure. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.884 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.10 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 4.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A, 1 sec | 83 | ASTM D2240 | |
| Shaw A, 5 seconds | 83 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 4.83 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 300 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 33.1 | MPa | ASTM D790A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -48.9 | °C | Internal method |
| Melting Temperature (DSC) | 114 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prixene® EL020E20 | POLYMAT | LLDPE | Prixene® |
| Evoprene™ COGEE 631 | AlphaGary | SEBS | Evoprene™ COGEE |
| HiFill® PA6 IM 40 Z | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| MAJORIS CG308X - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| LNP™ THERMOCOMP™ RF0029S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |