OP - PC/ABS 604-I

Category: PC+ABS , Polycarbonate + ABS
Manufacturer: Oxford Polymers
Trademark: OP - PC/ABS
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: KKrl6D_OP---PC-ABS-604-I.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
OP-PC/ABS 604-I is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America and is processed by injection molding. The main characteristics of OP-PC/ABS 604-I are: flame retardant/rated flame.
General Information
Features
  • General
Forms
  • Particle
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.15g/cm³ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/3.8 kg)8.5g/10 minASTM D1238
Molding Shrinkage - Flow 0.50 - 0.70%ASTM D955
MechanicalNominal ValueUnitTest Method
Tensile Strength ASTM D638
    Yield 52.4MPaASTM D638
    Fracture 53.8MPaASTM D638
Flexural Modulus 2210MPaASTM D790
Flexural Strength 72.4MPaASTM D790
ImpactNominal ValueUnitTest Method
Notched Izod Impact (4°C)480J/mASTM D256
Dart Drop Impact 36.2JASTM D3029
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, not annealed 113°CASTM D648
    1.8 MPa, not annealed 98.9°CASTM D648
FlammabilityNominal ValueTest Method
Flame Rating UL 94
    1.59 mm HBUL 94
    3.18 mm HBUL 94
Additional Information
Melt Mass -Flow Rate (MFR), ASTM D1238, 285°C/ 2.16kg: 3 to 14 g/10 min
InjectionNominal ValueUnit
Drying Temperature 76.7 - 82.2°C
Drying Time 3.0 - 4.0hr
Drying Time, Maximum 8.0hr
Rear Temperature 249 - 288°C
Middle Temperature 254 - 293°C
Front Temperature 260 - 302°C
Processing (Melt) Temp 274 - 302°C
Mold Temperature 71.1 - 93.3°C
Resin Grade Manufacturer Category Trademark
AKROMID® A3 GF 30 5 black (2180) AKRO-PLASTIC GmbH Nylon 66 AKROMID®
DOMAMID® 66G25V0P 1001 A DOMO Engineering Plastics SPA Nylon 66 DOMAMID®
Flontech® FT-BRR60-6 Guarniflon S.p.A. - Flontech Division PTFE Flontech®
Geon™ Vinyl Flexible F78E PolyOne Corporation PVC, Flexible Geon™ Vinyl Flexible
KRALASTIC® ST-200 Nippon A&L Inc. ABS KRALASTIC®