LNP™ STAT-KON™ MX01767C compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KIF2FP_LNP-STAT-KON-MX01767C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON MX01767C is a compound based on Polypropylene containing Proprietary Filler(s). Added features of this grade include: Electrically Conductive, Clean Compounding System. Also known as: LNP* STAT-KON* Compound PDX-M-01767 CCS Product reorder name: MX01767C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.978 | g/cm³ | |
| -- | 0.980 | g/cm³ | |
| Molding Shrinkage | Internal Method | ||
| Flow | 1.0 | % | |
| Across Flow | 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1770 | MPa | ASTM D638 |
| -- | 1570 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 32.0 | MPa | ASTM D638 |
| Yield | 31.0 | MPa | ISO 527-2/5 |
| Break 3 | 20.0 | MPa | ASTM D638 |
| Break | 22.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.5 | % | ASTM D638 |
| Yield | 6.6 | % | ISO 527-2/5 |
| Break 5 | 26 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 1490 | MPa | ASTM D790 |
| -- 7 | 1520 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 8 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 140 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 37.0 | J | ASTM D3763 |
| -- | 32.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 89.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 53.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 52.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 9.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 9.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 MI | NUREL, S.A. | Nylon 6 | Promyde® |
| Sylvin 8216-88 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| UTTAP QU HT530 GF | Ovation Polymers Inc. | Nylon, Unspecified | UTTAP |
| POLYfill PPHC TS25020 | Polykemi AB | PP, Unspecified | POLYfill |
| LNP™ LUBRICOMP™ Noryl_SPN422L compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |