VICTREX® PEEK 450FC30

Category:	PEEK , Polyetheretherketone
Manufacturer:	Victrex plc
Trademark:	VICTREX® PEEK
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KI8moG_VICTREX-PEEK-450FC30.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High performance thermoplastic material, 30% reinforced with carbon fibre / graphite / PTFE PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour black.

Tribological applications for high strength. Excellent wear resistance, very low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments.

General Information
Filler / Reinforcement	Carbon \Graphite \PTFE, 30% filler by weight
Features	Semicrystallization Low friction coefficient High strength Good liquidity Good chemical resistance Good wear resistance
Agency Ratings	FDA Food Exposure, Not Rated
Appearance	Black
Forms	Particles
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density ¹	1.45	g/cm³	ISO 1183
Spiral Flow ²
-- ³	8.00	cm	ExxonMobil Method
-- ⁴	38.0	cm	Internal method
Molding Shrinkage ⁵			ISO 294-4
Vertical flow direction : 200°C	0.70	%	ISO 294-4
Flow direction : 200°C	0.30	%	ISO 294-4
Water Absorption			ISO 62
23°C, 24 hr, 3.20 mm	0.040	%	ISO 62
Balance, 23°C, 3.20mm, 50% RH	0.30	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, 23°C)	83		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	12500	MPa	ISO 527-2
Tensile Stress			ISO 527-2
Fracture, 23°C	140	MPa	ISO 527-2
Fracture, 125°C	95.0	MPa	ISO 527-2
Fracture, 175°C	55.0	MPa	ISO 527-2
Fracture, 225°C	45.0	MPa	ISO 527-2
Fracture, 275°C	35.0	MPa	ISO 527-2
Tensile Strain (Break, 23°C)	2.2	%	ISO 527-2
Flexural Modulus (23°C)	11500	MPa	ISO 178
Flexural Stress (23°C)	230	MPa	ISO 178
Compressive Stress			ISO 604
23°C	170	MPa	ISO 604
120°C	110	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	5.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	35	kJ/m²	ISO 179/1U
Notched Izod Impact (23°C)	6.0	kJ/m²	ISO 180/A
Unnotched Izod Impact Strength (23°C)	35	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	315	°C	ISO 75-2/A
Glass Transition Temperature	143	°C	ISO 11357-2
Melting Temperature	343	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : < 143°C	1.5E-5	cm/cm/°C	ISO 11359-2
Flow : > 143°C	2.0E-5	cm/cm/°C	ISO 11359-2
Lateral : < 143°C	4.5E-5	cm/cm/°C	ISO 11359-2
Lateral : > 143°C	1.2E-4	cm/cm/°C	ISO 11359-2
Specific Heat (23°C)	1800	J/kg/°C	DSC
Thermal Conductivity (23°C)	0.87	W/m/K	ISO 22007-4
RTI Imp	180	°C	UL 746
RTI	240	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ⁶(23°C)	1.0E+10	ohms·cm	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Glow Wire Flammability Index (2.00 mm)	960	°C	IEC 60695-2-12
Oxygen Index	43	%	ISO 4589-2

Fill Analysis	Nominal Value	Unit	Test Method
Melt Viscosity (400°C)	550	Pa·s	ISO 11443

Injection	Nominal Value	Unit
Drying Temperature	120 - 150	°C
Drying Time	3.0 - 5.0	hr
Hopper Temperature	< 100	°C
Rear Temperature	365	°C
Middle Temperature	370 - 375	°C
Front Temperature	380	°C
Nozzle Temperature	385	°C
Mold Temperature	170 - 200	°C

Injection instructions
Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness

Note Message
1 .	Crystalline
2 .	Mold temperature: 200°C, melt temperature: 385°C
3 .	1 mm
4 .	3 mm
5 .	385°C nozzle
6 .	1V

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC C8085 FR	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
SIMONA® SIMOPOR-LIGHT	SIMONA AMERICA, Inc.	PVC, Unspecified	SIMONA®
APEX® 3211-80NT	Teknor Apex Company	PVC, Flexible	APEX®
AvaSpire® AV-848	Solvay Specialty Polymers	PAEK	AvaSpire®
POLYfill PPH T2020	Polykemi AB	PP Homopolymer	POLYfill