LNP™ LUBRICOMP™ D20001 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KGxEyF_LNP-LUBRICOMP-D20001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* D20001 is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Flame Retardant. Wear Resistant. Also known as: LNP* LUBRICOMP* Compound D-FR ECO Product reorder name: D20001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.57 | % | ISO 294-4 |
| Flow : 24 hr | 0.53 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2550 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 67.3 | MPa | ASTM D638 |
| Yield | 62.3 | MPa | ISO 527-2 |
| Break | 60.2 | MPa | ASTM D638 |
| Break | 54.5 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.5 | % | ASTM D638 |
| Yield | 4.3 | % | ISO 527-2 |
| Break | 6.5 | % | ASTM D638 |
| Break | 6.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2830 | MPa | ASTM D790 |
| -- | 2800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 103 | MPa | ASTM D790 |
| -- | 102 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.29 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 140 | J/m | ASTM D256 |
| 23°C 2 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1600 | J/m | ASTM D4812 |
| 23°C 3 | 100 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 51.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 97.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 89.4 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 94.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.7E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 254 to 288 | °C | |
| Mold Temperature | 37.8 to 65.6 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 15 FR | RTP Company | Nylon 66 | RTP |
| Rynite® 545 NC010 | DuPont Performance Polymers | PET | Rynite® |
| Toraycon® EC44G-30 | Toray Resin Company | PBT | Toraycon® |
| EMERGE™ PC 8410-15 | Trinseo | PC | EMERGE™ |
| Grilon® XE 5026 (BG-30 H) | EMS-GRIVORY | Nylon 6 | Grilon® |