Electrafil® J-50/CF/30/TF/15
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KGlID4_Electrafil-J-50-CF-30-TF-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-50/CF/30/TF/15 is a polycarbonate (PC) product that contains 30% carbon fiber reinforced materials. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-50/CF/30/TF/15 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 117 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 1.7 | % | ASTM D638 |
| Flexural Modulus (23°C) | 13800 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 193 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| CLTE - Flow | 1.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+3 | ohms | ASTM D257 |
| Volume Resistivity | 55 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257: 1E3-1E4 ohmsVolume Resistivity, ASTM C611: 10-100 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 8.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 302 - 310 | °C | |
| Middle Temperature | 310 - 327 | °C | |
| Front Temperature | 316 - 327 | °C | |
| Nozzle Temperature | 310 - 321 | °C | |
| Processing (Melt) Temp | 304 - 321 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.172 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A23300 X | 4Plas | Nylon 66 | 4MID® |
| Aurora PVC AP1250 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Flexiblend® PP-1300 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP+EPDM | Flexiblend® |
| LNP™ THERMOCOMP™ LF002XXP-WT02005 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ LX97024 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ THERMOCOMP™ |