SCHULAFORM® 9 D LE NATURAL
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KGheUU_SCHULAFORM9DLENATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flow Polyoxymethylene grade with low emissions for automotive applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 21.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 137 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 62.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 9.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 94.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 147 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | |||
| VDA 277, TVOC (total organic compounds) | µgC/g | VDA 277 | |
| VDA 278, Fog (condensable compounds) | µgC/g | VDA 278 | |
| VDA 278, VOC (volatile organic compounds) | µgC/g | VDA 278 | |
| Formaldehyde Emissions | mg/kg | VDA 275 | |
| Odor | 3.00 | VDA 270 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 200 - 210 | °C | |
| Mold Temperature | 60 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 UV | RTP Company | Nylon 66 | RTP |
| Taitacell EPS 321LMM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Haysite Plastics H261 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| HANWHA LDPE 5321 (Film) | Hanwha Chemical | LDPE | HANWHA LDPE |
| INELEC PPACF10 | Infinity LTL Engineered Compounds | PPA | INELEC |