EXTEM™ XH2315 resin
| Category: | PI, TP , Thermoplastic Polyimide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | EXTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KGUgLl_EXTEMXH2315resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extem XH2315 Resin. Also UL rating V094 at 0.75 and V0,5VA at 1.0 and 1.5-1.65 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (367°C/6.6 kg) | 4.0 | g/10 min | ASTM D1238 |
| Water Absorption 1(23°C, 24 hr) | 0.59 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 10200 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 156 | MPa | ASTM D638 |
| Yield | 147 | MPa | ISO 527-2/5 |
| Fracture 4 | 156 | MPa | ASTM D638 |
| Fracture | 147 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 5 | 3.0 | % | ASTM D638 |
| Yield | 2.0 | % | ISO 527-2/5 |
| Fracture 6 | 3.0 | % | ASTM D638 |
| Fracture | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 7 | 8960 | MPa | ASTM D790 |
| -- 8 | 9000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 200 | MPa | ISO 178 |
| Yield, 50.0mm span 9 | 206 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 10(23°C) | 24 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 86 | J/m | ASTM D256 |
| 23°C 11 | 5.7 | kJ/m² | ISO 180/1A |
| Reverse Notch Izod Impact (3.20 mm) | 320 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 8.20 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 257 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 254 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 255 | °C | ASTM D648 |
| Vicat Softening Temperature | 267 | °C | ASTM D1525 12 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : 23 to 150°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 23 to 150°C | 5.3E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.40 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 175 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 70 | % | |
| Rear Temperature | 360 - 380 | °C | |
| Middle Temperature | 370 - 395 | °C | |
| Front Temperature | 380 - 405 | °C | |
| Nozzle Temperature | 375 - 400 | °C | |
| Processing (Melt) Temp | 380 - 405 | °C | |
| Mold Temperature | 150 - 175 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 70 - 100 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Results measured at 48 hrs |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | Type 1, 5.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 2412GHF8 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| VESTODUR® GF30 | Evonik Industries AG | PBT | VESTODUR® |
| TORZEN® G3300HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| Desmopan® 795 U | Covestro - PUR | TPU, Unspecified | Desmopan® |
| Sylvin 8482-72 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |