Promyde® B30 P2 MI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | NUREL, S.A. |
| Trademark: | Promyde® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFyixB_Promyde-B30-P2-MI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Promyde B30 P2 MI is a Polyamide 6 impact modified, heat stabilised with equilibrated mechanical properties and optimal flow behaviour. CHARACTERISTICS Promyde B30 P2 MI is a polyamide 6 impact modified and heat stabilized. APPLICATIONS Promyde B30 P2 MI allows a fast and efficient mould filling, and easy mould release, that combined with its excellent mechanical and impact resistant properties make it suitable for applications sensitive to breakage by impact (e.g. housings, fittings, small parts and anchors). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.10 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 100 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ||||
| Vertical flow direction | 0.80 - 1.1 | -- | % | |
| Flow direction | 0.90 - 1.1 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Viscosity Number 1(H2SO4 (Sulphuric Acid)) | 125 | -- | cm³/g | ISO 960 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2800 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 75.0 | 35.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 5.0 | 25 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 25 | 180 | % | ISO 527-2/50 |
| Flexural Modulus 2(23°C) | 2300 | 750 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 85.0 | 25.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 14 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 150 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 222 | -- | °C | ISO 3146 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 80°C | 7.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.50 | 7.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.026 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Back pressure: moderate |
| Note Message | |
|---|---|
| 1 . | 0,005 g/ml H2SO4 |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax 7823 | LyondellBasell Industries | PP Copolymer | Pro-fax |
| Iupilon® GPF2040DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LNP™ LUBRICOMP™ PFP36 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ LUBRICOMP™ |
| Sylvin 7833-85 White 1574 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sumiliteresin® ECP-354 | SBHPP | Epoxy | Sumiliteresin® |