Lighter™ C98
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Equipolymers |
| Trademark: | Lighter™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFcx9v_Lighter-C98.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lighter Resins are polyethylene terephthalate produced from PTA and MEG. These are specifically designed for the production of beverage, food and other liquid containers for thermoforming. There are several LIGHTER PET polymers, designed for the specific performance requirements of different applications, including very good mechanical properties, excellent clarity, and a wide processing range on all injection and stretch blow molding machines. LIGHTER C98 is particularly suitable for bottling mineral water since it is designed specifically to minimize the formation of acetaldehyde. In general this grade is recommended for bottles for both still and carbonated mineral water. LIGHTER C98 is also suitable for the production of extruded thermoformable sheets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density | 0.88 | g/cm³ | Internal Method |
| Viscosity Number (Reduced Viscosity) | 98.0 | ml/g | Internal Method |
| Moisture Content | < 4000 | ppm | Internal Method |
| Acetaldehyde | < 1.0 | ppm | Internal Method |
| Crystallinity | > 50 | % | Internal Method |
| Intrinsic Viscosity | 0.82 to 0.86 | dl/g | Internal Method |
| Weight - 100 Granules | 1.5 | g | Internal Method |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color Coordinate - b | < 2.00 | Internal Method | |
| Fine Particles | < 500 | ppm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 24.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.0 | % | |
| Break | 250 | % | |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 78.0 | °C | Internal Method |
| Vicat Softening Temperature | 77.0 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 247 | °C | Internal Method |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® M-1858-GL 06 | Unipack Plasindo | PVC, Unspecified | polyvic® |
| Trithene® TS 7028 | Petroquimica Triunfo | LDPE | Trithene® |
| Karina IVORY PVC COMPOUND -E 90850-35/1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Kepital® ET-20 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Jampilen RP348U | Jam Polypropylene Company | PP Random Copolymer | Jampilen |