Celanex® 6407
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFXbP8_Celanex-6407.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 6407 is a 30% glass/mineral reinforced resin particularly suited for large exterior automotive components, where extended flow, flatness and good surface appearance is essential. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.52 | g/cm³ | ASTM D792 |
| -- | 1.51 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 12 - 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.40 | % | ASTM D955 |
| Vertical flow direction | 0.98 | % | ISO 294-4 |
| Flow direction | 0.30 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 86.2 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 3.0 | % | ASTM D638 |
| Fracture | 2.1 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 209 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 212 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 175 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 172 | °C | ISO 75-2/A |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 235 - 255 | °C | |
| Nozzle Temperature | 240 - 265 | °C | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 65.0 - 96.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 265°CZone 4 Temperature: 240 to 265°CFeed Temperature: 230 to 250°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GTPR-1860F | S&E Specialty Polymers, LLC | TPE | S&E PVC |
| Trexprene® A88BU | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| AIE PC/ABS A2200HF-T5 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| ALFATER XL® D50I 2GP0050 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Diablend 4500/V0 HF | DTR S.r.l. (Develop Thermoplastic Resins) | PC+ABS | Diablend |