TROGAMID® T T5000 Datasheet,Nylon 6/3T,Evonik Industries AG-SHANGHAI SUSHENG

Message
TROGAMID® T and BX consist of terephthalic acid and 2,2,4- /2,4,4-trimethyl hexamethylene diamine, a chemical composition that is responsible for their amorphous structure. This makes TROGAMID® T transparent in contrast to the semi-crystalline high-performance plastics of High Performance Polymers. The amorphous structure also results in low molding shrinkage and low tendency to warp. In addition to the basic products, a range of specially equipped compounds is also available. The product line fits a wide range of applications and satisfies many requirement profiles. TROGAMID® T5000 Permanently transparent polyamide for injection molding, extrusion, and blow molding; no additives.

General Information
Features	Amorphous Copolymer Good Chemical Resistance Good Electrical Properties Good Thermal Stability High Viscosity Low Shrinkage Low Warpage
Uses	Electrical/Electronic Applications Filters Gears Machine/Mechanical Parts
Appearance	Clear/Transparent Colors Available Natural Color
Processing Method	Blow Molding Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.12	g/cm³	ISO 1183
Viscosity Number	132	cm³/g	ISO 307

Hardness	Nominal Value	Unit	Test Method
Shore Hardness (Shore D)	87		ISO 868
Ball Indentation Hardness	155	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2800	MPa	ISO 527-2
Tensile Stress (Yield)	90.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	8.0	%	ISO 527-2/50
Nominal Tensile Strain at Break	> 50	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	2300	MPa
1000 hr	1100	MPa
Flexural Modulus	3000	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C, Complete Break	7.0	kJ/m²
0°C, Complete Break	11	kJ/m²
23°C, Complete Break	12	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	No Break
0°C	No Break
23°C	No Break

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	145	°C	ISO 75-2/B
1.8 MPa, Unannealed	130	°C	ISO 75-2/A
Glass Transition Temperature ¹	150	°C	ISO 11357-2
Vicat Softening Temperature
--	155	°C	ISO 306/A
--	150	°C	ISO 306/B
CLTE			ISO 11359-2
Flow : 23 to 80°C	5.5E-5	cm/cm/°C
Transverse : 23 to 80°C	5.5E-5	cm/cm/°C
RTI Elec			UL 746
0.800 mm	100	°C
1.60 mm	100	°C
3.00 mm	100	°C
RTI Imp			UL 746
1.60 mm	80.0	°C
3.00 mm	85.0	°C
RTI Str			UL 746
1.60 mm	85.0	°C
3.00 mm	90.0	°C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+13	ohms	IEC 60093
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Electric Strength	25	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 50 Hz	4.20
23°C, 1 MHz	3.40
23°C, 100 MHz	4.60
Dissipation Factor			IEC 60250
23°C, 50 Hz	0.021
23°C, 1 MHz	0.028
23°C, 100 MHz	0.025
Comparative Tracking Index			IEC 60112
-- ²	575	V
Solution A	600	V

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	V-2
1.60 mm	V-2
Glow Wire Flammability Index (1.00 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.00 mm)	900	°C	IEC 60695-2-13

Note Message
1 .	10 K/min
2 .	100 drops value

Category:	Nylon 6/3T , Polyamide 6/3T Copolymer
Manufacturer:	Evonik Industries AG
Trademark:	TROGAMID® T
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	KFXVIS_TROGAMID-T-T5000.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SLOVAMID® 6 GF 30 LS	Plastcom	Nylon 6	SLOVAMID® 6
Witcom ABS AS	Witcom Engineering Plastics B.V.	ABS	Witcom ABS
EcoPaXX® Q-HGM24	DSM Engineering Plastics	Nylon 410	EcoPaXX®
LNP™ STAT-KON™ OX00428 compound	SABIC Innovative Plastics	PPS, Linear	LNP™ STAT-KON™
KMI PP KM-4494ZW	KMI Group, Inc.	PP Impact Copolymer	KMI PP