SEPAZ™ K435CTS
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KFPbCB_SEPAZ-K435CTS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ K435CTS is a Polyphenylene Sulfide (PPS) product filled with 20% carbon fiber. It is available in Asia Pacific. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.10 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 161 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 14700 | MPa | ASTM D790 |
| Flexural Strength | 224 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 47 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 135 to 163 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Formolene® HP4306 | Formosa Plastics Corporation, U.S.A. | HDPE Copolymer | Formolene® |
| FORMULA P COMP 6220 M1 | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| Hy-Vin® XX79945 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Paraclean® 33L50 | INSA | NBR | Paraclean® |
| Star L POK D51 - BK84034 | Eurostar Engineering Plastics | PK | Star L |