Order Products : sales@su-jiao.com
LNP™ LUBRICOMP™ WX12001J compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KF5sh2_LNP-LUBRICOMP-WX12001J-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUBRICOMP* WX12001J is an internally lubricated PBT compound with excellent wear and friction properties designed for Healthcare applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 25.0 | cm³/10min | ISO 1133 |
| Water Absorption 1(23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 56.0 | MPa | |
| Break | 54.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 10 | % | |
| Break | 13 | % | |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength 4(23°C) | 3.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5(23°C) | 47 | kJ/m² | ISO 180/1U |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50% RH |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 15S3304 | The Matrixx Group, Inc. | PP, Unspecified | Matrixx |
| Sylvin 7833-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| KumhoSunny PET HEG3620FG | Shanghai KumhoSunny Plastics Co., Ltd. | PET | KumhoSunny PET |
| POLYCOMPO PE 5000SR | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Axiall PVC 19781 | Axiall Corporation | PVC, Flexible | Axiall PVC |