Hostalen GM 9310 C black
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KDQDRX_Hostalen-GM-9310-C-black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen GM 9310 C black is a electrically conductive high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for pipes and fittings for application in explosion-proof areas. The product provides good long term hydrostatic strength. It is not intended for medical, pharmaceutical and food contact applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 4.5 | g/10 min | ISO 1133 |
| Carbon Black Content | 10 | % | ISO 6964 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Creep Modulus 1 | 1.40 | GPa | DIN 19537-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | 20 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Staudinger Index | 290 | cm³/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 66 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 55.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1250 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 7.0 | % | ISO 527-2/50 |
| Tensile Creep Modulus (1 hr) | 780 | MPa | ISO 899-1 |
| Flexural Stress (3.5% Strain) | 24.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 83.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+5 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 1 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT019 | Sasol Polymers | LDPE | Sasol Polymers PE |
| TEREZ PBT 7100 GF 30 | TER HELL PLASTIC GMBH | PBT | TEREZ PBT |
| BESTNYL SE35VI02AX | Triesa Plastics | Nylon 66 | BESTNYL |
| DAI-EL™ G-751 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Geon™ Vinyl Flexible R246AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |