Latilub 80-10T G/40
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilub |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KCRsGo_Latilub-80-10T-G-40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Self-lubricating product based on Polyphenylene Sulphide (PPS). PTFE. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.72 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Vertical flow direction : 2.00mm | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.10 - 0.25 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 14500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Coefficient of Friction | ASTM D1894 | ||
| With self-dynamics | 0.23 | ASTM D1894 | |
| With Self-Static | 0.26 | ASTM D1894 | |
| Wear Factor | 100 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 280 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 265 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 - 310 | °C | |
| Mold Temperature | 130 - 150 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ B70 GK30 BK186 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Anjacom® R050/75S Black 91012 | Almaak International GmbH | PC+ABS | Anjacom® |
| KRALASTIC® K-2938FSR-1 | Nippon A&L Inc. | ABS | KRALASTIC® |
| PEARLSTICK® 48-60/30 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |
| Trilliant™ HC 2020-0001 FR | PolyOne Corporation | Copolyester | Trilliant™ HC |