TECHNO ABS F1150
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techno Polymer Co, Ltd. |
| Trademark: | TECHNO ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KBk1SH_TECHNO-ABS-F1150.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TECHNO ABS F1150 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Asia Pacific or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 52 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 46.1 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2550 | MPa | ASTM D790 |
| -- | 2270 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 74.5 | MPa | ASTM D790 |
| -- | 71.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 90.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, ALL | V-2 | ||
| 2.50 mm, ALL | V-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Rear Temperature | 180 to 230 | °C | |
| Middle Temperature | 180 to 230 | °C | |
| Front Temperature | 180 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP378T | LyondellBasell Industries | PP Random Copolymer | Purell |
| 3M™ Dyneon™ Fluoroplastic FEP 6303Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Cri-Line LS-918 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| ISPLEN® PP 084 D2M | REPSOL | PP Homopolymer | ISPLEN® |
| Adflex 7635 XCP | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |