LNP™ LUBRICOMP™ KAL22 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KBI2fL_LNPLUBRICOMPKAL22compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KAL22 is a compound based on Acetal Copolymer resin containing 10% PTFE, 10% Aramid Fiber. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KAL-4022 Product reorder name: KAL22 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.46 | g/cm³ | ASTM D792 |
| -- | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow 1 | 1.8 - 2.2 | % | Internal method |
| Flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Transverse flow : 24 hours | 2.0 - 4.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 3640 | MPa | ASTM D638 |
| -- | 3460 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 57.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 58.0 | MPa | ASTM D638 |
| Fracture | 56.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 6.5 | % | ASTM D638 |
| Yield | 6.3 | % | ISO 527-2/5 |
| Fracture 5 | 7.4 | % | ASTM D638 |
| Fracture | 7.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3090 | MPa | ASTM D790 |
| -- 7 | 3080 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.23 | ASTM D3702 Modified | |
| With Self-Static | 0.16 | ASTM D3702 Modified | |
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Washer | 8.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 54 | J/m | ASTM D256 |
| 23°C 8 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 510 | J/m | ASTM D4812 |
| 23°C 9 | 32 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 162 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 132 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 87.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® COPP 10.2.0 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |
| POLYshine PBT C213 GF15 FR | Polykemi AB | PBT+PET | POLYshine |
| TEKNIFLEX® MED 3012-0180 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| Stat-Tech™ PC-CB2/000 CR | PolyOne Corporation | PC | Stat-Tech™ |
| Compoceran E102B | Arakawa Chemical Industries, Ltd. | Epoxy | Compoceran |