Matrixx TPP1B10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KAqAkN_Matrixx-TPP1B10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Matrixx TPP1B10 is a polypropylene material, which contains 10% talc filler. This product is available in North America and is processed by injection molding. The main characteristics of Matrixx TPP1B10 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.90 - 1.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.8 | MPa | ASTM D638 |
| Flexural Modulus - Tangent | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Dart Drop Impact | < 1.13 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.8 | °C | ASTM D648 |
| RTI | 65.6 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with Matrixx test methods. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 177 - 221 | °C | |
| Middle Temperature | 177 - 221 | °C | |
| Front Temperature | 177 - 221 | °C | |
| Processing (Melt) Temp | 199 - 227 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.138 - 2.07 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Drying not normally requiredInjection Booster Pressure: Maximum without flash, 60% of machine maximum, targetScrew Speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ FR H6 T/05 H XF V0 NATURAL 70 | PolyOne Corporation | PP Homopolymer | Maxxam™ FR |
| SKYGREEN® S2008 | SK Chemicals | PETG | SKYGREEN® |
| ALTECH® PA66 A 2030/516 GF30 IM | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| DIC.PPS CZ-1030 | DIC Corporation | PPS | DIC.PPS |
| LNP™ THERMOCOMP™ RC003SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |