Fiberfil® PP-61/VO/NH
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KA6lRg_Fiberfil-PP-61-VO-NH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fiberfil®PP-61/VO/NH is a polypropylene copolymer material,. This product is available in North America,. Fiberfil®The main features of PP-61/VO/NH are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 - 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 1.3 - 1.7 | % | ASTM D955 |
| 6.35 mm | 1.8 - 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 - 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1720 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 19.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 13 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 1520 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 22.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 71.1 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.8 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 182 - 199 | °C | |
| Middle Temperature | 193 - 210 | °C | |
| Front Temperature | 188 - 204 | °C | |
| Nozzle Temperature | 182 - 193 | °C | |
| Processing (Melt) Temp | 193 - 216 | °C | |
| Mold Temperature | 32.2 - 71.1 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ F113G | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| RTP ESD C 2700 S-50A | RTP Company | SEBS | RTP |
| Sylvin 8716-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Hypro® PP-CP 10/10 | Entec Polymers | PP Impact Copolymer | Hypro® |
| Resilience™ LS21150E | PolyOne Corporation | PVC, Rigid | Resilience™ |