Alkamax® ML 1810PS
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkamax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KA22qY_Alkamax-ML-1810PS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Alkamax® ML1810PS is a metallocene linear low density polyethylene copolymer.This metallocene grade has excellent processability permitting higher production rates. It is designed for high performance film applications requiring maximum toughness and excellent sealing performance. Alkamax ML1810PS is formulated with a high slip level, process stabilisation, process aid and antiblocking additive. Alkamax ML1810PS is intended for applications requiring high performance polyethylene resins combined with low COF. Films produced with Alkamax ML1810PS have outstanding toughness, making this grade ideal for use in heavy duty applications or for downgauging existing film structures. In addition, the high performance sealing and hot tack properties of this grade combined with its excellent optical properties make it ideal for lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 2% Secant, MD : 50 µm | 180 | MPa | |
| 2% Secant, TD : 50 µm | 190 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 50 µm | 11.0 | MPa | |
| TD : Yield, 50 µm | 11.0 | MPa | |
| MD : Break, 50 µm | 39.0 | MPa | |
| TD : Break, 50 µm | 34.0 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break, 50 µm | 720 | % | |
| TD : Break, 50 µm | 740 | % | |
| Dart Drop Impact 4 | > 1300 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 580 | g | |
| TD : 50 µm | 660 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 5(45°) | 60 | ASTM D2457 | |
| Haze 6(50.0 µm) | 13 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | F50 |
| 5 . | (10% LDPE blended) |
| 6 . | (10% LDPE blended) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-MK21E | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| ULTEM™ JD4901 resin | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ |
| Baytec® RTC V85 Component A (120\-\95\5) | Covestro - PUR | PUR-Ether/MDI | Baytec® |
| Gallonprene® GP520-7509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| LubriOne™ AT-000/05T 2S | PolyOne Corporation | Acetal (POM) Copolymer | LubriOne™ |