Machine Cast MC-165 A/B
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | Machine Cast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K85BGH_Machine-Cast-MC-165-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The MC-165 A/B system is a production oriented fast gel and fast de-mold system. It features a mix ratio and working time ideal for machine dispensing and rapid part mold cycling, for production applications. It also features excellent adhesion to metal, plastics, wood, and is ideal for many potting applications. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 0.988 | g/cm³ | |
| -- | 1.10 | g/cm³ | ASTM D792 |
| -- 2 | 1.14 | g/cm³ | |
| Shrinkage 3 | 0.70 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Demold Time (25°C, 9.53 mm) | 1.5 - 2.0 | hr | |
| Gel Time | 2.3 | min | |
| Work Time 4(25°C) | 2.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time (25°C) | 5.0 - 7.0 | day |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 - 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 254 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 18.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 35 | % | ASTM D638 |
| Flexural Modulus | 293 | MPa | ASTM D790 |
| Flexural Strength | 9.38 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 46.8 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | 80 | J/m | ASTM D256 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.57 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.033 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio calculated by weight: 87, mixing ratio calculated by capacity: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity (25°C) | 770 | cP | Brookfield |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Note: Physical properties obtained from test specimens post cured per recommended procedure.In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160° - 180°F (71° - 82°C). Support of the part may be required to prevent part deformation during heat cure. |
| Note Message | |
|---|---|
| 1 . | Part B |
| 2 . | Part A |
| 3 . | 12"x1/2"x1/2" |
| 4 . | 100g mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultra Purge PET-E | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |
| XANTAR® MX 1081 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Nypol® PA B3 G50 NTLA010 NT322 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Celstran® PP-GF50-02-Black | Celanese Corporation | PP, Unspecified | Celstran® |
| EMOPLEN® CP FR V0 | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |