AKROLEN® PP GFM 25/15 black 950088 (1415)
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K6ktAC_AKROLENPPGFM2515black9500881415.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLEN® PP GFM 25/15 black 950088 (1415) is a 25% glass fibre reinforced, 15% mineral-filled polypropylene with good surface and dimensional stability Applications are mainly thin wall housings for electronic parts in the automotive industry with operation temperatures up to 100°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.21 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 13.5 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6600 | MPa | ISO 178 |
| Flexural Stress 2 | 105 | MPa | ISO 178 |
| Flexural Strain at Break 3 | 3.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 42 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 163 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 150 | °C | ISO 75-2/A |
| Melting Temperature 4 | 167 | °C | DIN EN 11357-1 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 2.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.6 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.0 mm) | 750 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2 mm/min |
| 4 . | 10°C/min |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® T2000HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| TOTAL Polypropylene PPH 3060 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Ferro PP LPP30BK86HB | Ferro Corporation | PP Copolymer | Ferro PP |
| Hanwha Total PP BI616 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Hostacom PPU X9067HS D82513 | LyondellBasell Industries | PP Copolymer | Hostacom |