VITAMIDE® BW10NT6621
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K6gMip_VITAMIDE-BW10NT6621.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® BW10NT6621 is a Polyamide 6 (Nylon 6) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption | |||
| 24 hr | 2.6 | % | ASTM D570 |
| 23°C, 24 hr | 2.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 70.0 | MPa | ISO 527-2 |
| -- | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2700 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 105 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 5.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 175 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 218 | °C | ISO 1218, ASTM D1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 13 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | 600 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A 50W 100 M NAT 5770 | Radici Plastics | Nylon 66 | Radilon® |
| Utomer UT370 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| DuPure® U 76 | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |
| FRAGOM XLC/900 OR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Hyundai EP PPC HP908H | HYUNDAI EP Co., Ltd. | PP Copolymer | Hyundai EP PPC |