Hax™ HFX 519
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Fainplast Compounds S.r.l |
| Trademark: | Hax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K5cQfg_Hax-HFX-519.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GRAFTED HALOGEN FREE, FLAME RETARDANT AND LOW SMOKE EMISSION COMPOUND, CURABLE BY EXPOSURE TO MOISTURE FOR CABLE INSULATION AND SHEATING This product is a LSFOH silane grafted compound for cable insulation and sheating, Cross-linkable by heat and moisture by previous addition of a suitable catalyst masterbatch (SIOPLAS method). It is highly recommended to store separately the grafted compound and the catalyst, as prescorching may take place during the reactive extrusion. The properties of this compound meet the requirements of VDE 0266 type HXI1 & HXM1, EN 50363-0 type G9-G10 & M2, VDE 0207 part 23 type HJ1, BS 50363-5:2005 type EI5, CEI 20-91 type G21-M21, TUV2pfg1169-082007solar insulation and sheath |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (150°C/21.6 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1(100°C, 1 hr) | < 4.0 | % | IEC 60811 |
| Water Absorption - 24 hrs (100°C) 2 | < 5.00 | mg/cm² | IEC 60811 |
| pH | > 4.3 | EN 50267-2-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 3 | IEC 60811 | ||
| Elongation under load : 200°C | 30 | % | |
| Elongation under load : 250°C | 30 | % | |
| Permanent elongation after cooling : 200°C | 0.0 | % | |
| Permanent elongation after cooling : 250°C | 5.0 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 10.0 | µS/mm | EN 50267-2-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gas Evolved Acidity | |||
| HCl & HBr | < 0.50 | % | EN 50267-2-1 |
| HF | < 0.10 | % | EN 60684-2 |
| Knife Penetration (100°C) 4 | < 50 | % | IEC 60811 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 38 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | IEC 60811 | ||
| Break 5 | 12.0 | MPa | |
| Break | 11.0 | MPa | |
| Tensile Strain | IEC 60811 | ||
| Break 6 | 270 | % | |
| Break | 350 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 20°C 7 | 9.0E+15 | ohms·cm | |
| 20°C | 1.0E+16 | ohms·cm |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 30 | % | ISO 4589-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 120 to 140 | °C | |
| Cylinder Zone 2 Temp. | 120 to 140 | °C | |
| Cylinder Zone 3 Temp. | 130 to 150 | °C | |
| Cylinder Zone 4 Temp. | 130 to 150 | °C | |
| Cylinder Zone 5 Temp. | 130 to 150 | °C | |
| Adapter Temperature | 130 to 150 | °C | |
| Die Temperature | 150 to 180 | °C |
| Note Message | |
|---|---|
| 1 . | After Crosslinking |
| 2 . | After Crosslinking |
| 3 . | 15mins, 0.2 N/mm², After Crosslinking |
| 4 . | k = 1.0, After Crosslinking |
| 5 . | After Crosslinking |
| 6 . | After Crosslinking |
| 7 . | After Crosslinking |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1305 TFE 15 P-1 | RTP Company | PPS | RTP |
| RTP ESD C 201 | RTP Company | Nylon 66 | RTP |
| Sicoflex S309 | Ravago Group | ABS | Sicoflex |
| Vyncolit® RX®2-520 | Vyncolit N.V. | DAP | Vyncolit® |
| GAPEX® APP40GR17HB-NA | Ferro Corporation | PP Homopolymer | GAPEX® |