4TECH® 9A22730 H
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | 4Plas |
| Trademark: | 4TECH® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K3dXFG_4TECH-9A22730-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4TECH 9A22730 H is a Standard Flow 30% Carbon Fibre Reinforced Heat Stabilised PA66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 2.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 18000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 200 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 255 | °C | ISO 75-2/B |
| Melting Temperature 2 | 265 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 70.0 - 110 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 60 - 80 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® FX50 | A. Schulman Europe | ABS | RONFALIN® |
| TOTAL Polypropylene PPC 4944WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| XYRON™ X352V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Casico™ FR4804 | Borealis AG | PE, Unspecified | Casico™ |
| Sylvin 3299-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |