Styrolution PS 153A
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K18CG9_Styrolution-PS-153A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolution PS 153A is an antistatic modified, general purpose polystyrene grade with a good flow characteristic. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 35.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 1.5 | % | ISO 527-2 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 1 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 280 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| apilon 52® TL 65 | API SpA | TPU-Polyether | apilon 52® |
| EcoLon® MRGF1937-BK1 | Wellman Engineering Resins | Nylon 66 | EcoLon® |
| EMVIN 733 | Intergulf Empol | PVC, Flexible | EMVIN |
| Optix® CA-61 FDA | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |
| Shida 3210 | JINJIANG City SHIDA Plastic Fine Co., Ltd. | TPE | Shida |