LNP™ THERMOCOMP™ RX98372H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K0pZgh_LNPTHERMOCOMPRX98372Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX98372H is a compound based on Nylon 66 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound PDX-R-98372 EES HC Product reorder name: RX98372H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.26 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 23200 | MPa | ASTM D638 |
| Tensile Strength (Break) | 237 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 20000 | MPa | ASTM D790 |
| Flexural Strength | 359 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 257 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novamid® 1010C2 | DSM Engineering Plastics | Nylon 6 | Novamid® |
| AVP™ RYY13UVCP | SABIC Innovative Plastics | Nylon 66 | AVP™ |
| Karina RED PVC COMP. -E 850-42/231-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lucent PP CPP-140 | Lucent Polymers, Inc. | PP Homopolymer | Lucent PP |
| Sylvin 83054-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |