LNP™ THERMOCOMP™ UC008H compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | K07ROq_LNPTHERMOCOMPUC008Hcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UC008H is a compound based on Polyphthalamide resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound UC-1008 Product reorder name: UC008H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.70 - 0.90 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.70 - 0.90 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.40 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.46 - 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 33800 | MPa | ASTM D638 |
| -- | 35500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 261 | MPa | ASTM D638 |
| Fracture | 232 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.0 | % | ASTM D638 |
| Fracture | 1.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 26800 | MPa | ASTM D790 |
| -- | 26600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 441 | MPa | ASTM D790 |
| -- | 425 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 7.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 330 | J/m | ASTM D4812 |
| 23°C 3 | 45 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.00 | J | ASTM D3763 |
| -- | 5.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | > 249 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | > 250 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+4 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AY13 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Ferro PP TPP30AE85HB TAN | Ferro Corporation | PP Homopolymer | Ferro PP |
| HiFill® PA4/6 GF30 FR HS L | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| INEOS LLDPE LL6930AA | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| Petro Rabigh PE F0554 | Rabigh Refining & Petrochemical Co. | HDPE | Petro Rabigh PE |