| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | KPOL Chem Co. |
| Trademark: | KPOL-HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Izydol_KPOL-HDPE-HD-K-0-65-964.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Density Polyethylene Homopolymer Extrusion-Blow Molding Applications
Characterisitics
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.964 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.65 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1 | |||
| 50°C, 3.18 mm, 100% Igepal CO-630, F50 | 15.0 to 20.0 | hr | ASTM D1693A |
| 50°C, 1.91 mm, 100% Igepal CO-630, F50 | 8.00 to 10.0 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 1 sec, 23°C) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 30.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | > 300 | % | ASTM D638 |
| Flexural Modulus - Tangent 4(3.20 mm) | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 126 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 79.0 | °C | ASTM D648 |
| Brittleness Temperature 5 | < -76.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 130 | °C | ASTM D1525 6 |
| Note Message | |
|---|---|
| 1 . | Grooved Specimen |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| 5 . | F50; 25 lbfXin |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P598 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| TECHNYL® C R 218 V30 BLACK 1 N | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| Topolymer® 3211 | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| NOTIO™ PN-2060 | Mitsui Chemicals America, Inc. | TPE | NOTIO™ |
| Fluoroplex MB 555 - GML | UNIFLON | PTFE | Fluoroplex |