EMERGE™ PC 8600-7
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IyhDtV_EMERGE-PC-8600-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8600 is a translucent ignition-resistant polycarbonate resin. This resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It is an easy flow PC resin suitable for use in injection molded applications. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2210 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 60.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 57.9 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 6.2 | % | |
| Break, 3.20 mm, Injection Molded | 110 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2400 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 93.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 750 | J/m | ASTM D256 |
| Instrumented Dart Impact 1(23°C, 3.20 mm, Injection Molded, Total Energy) | 58.8 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 139 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| Vicat Softening Temperature | 149 | °C | ASTM D1525 2 |
| CLTE - Flow (-40 to 82°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (3.20 mm) | 125 | °C | UL 746 |
| RTI Imp (3.20 mm) | 125 | °C | UL 746 |
| RTI Str (3.20 mm) | 125 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index 4(1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index 5 | 35 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 271 to 288 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Note Message | |
|---|---|
| 1 . | 3.39 m/sec |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU H890FNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Witcom PP AS-S | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Bayfill® EA 2003 (5 pcf) | Covestro - PUR | PUR-Ether/MDI | Bayfill® |
| CoREZYN® CORVE8100-50 | Interplastic Corporation | Vinyl Ester | CoREZYN® |
| Karina BLACK PVC COMPOUND 600D48/1-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |