LubriOne™ NN-30GF/13T-2S Black
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IwhTeB_LubriOne-NN-30GF-13T-2S-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 1.0 to 2.0 | % | |
| Water Absorption (24 hr) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8760 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 130 | MPa | |
| Break 2 | 130 | MPa | |
| Tensile Elongation 3(Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 6690 | MPa | ASTM D790 |
| Flexural Strength | 193 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.15 | ||
| vs. Steel - Static | 0.28 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.18 mm | 257 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 242 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 288 to 299 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 EM | RTP Company | PC | RTP |
| Sanren DJ210 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Mirakutoran® TPU E190 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sinpolene HFR8294 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Vipel® K022-CDC-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |