FLEXAREN® 14006
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Innospec Leuna GmbH |
| Trademark: | FLEXAREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IuLZrK_FLEXAREN-14006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FLEXAREN® 14006 - high quality ethylene vinyl acetate copolymer with 14% content of vinyl acetate. Manufactured by high pressure tubular process FLEXAREN® 14006 is more elastic than LDPE and compatible with a wide range of polymers. It can be processed with the same equipment. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 0.934 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 14.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A | 91 | ||
| Shore D | 35 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1BA | ||
| Break | 17.0 | MPa | |
| 50% Strain | 4.10 | MPa | |
| Tensile Strain (Break) | > 750 | % | ISO 527-2/1BA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ISO 306/A |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Processing Temperature | 100 to 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® Electro 242-0 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| VITAMIDE® BT36WT6427 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| YUCLAIR® FV149M | SK Global Chemical | LLDPE | YUCLAIR® |
| HiPrene® HT42WGT | GS Caltex | PP, Unspecified | HiPrene® |
| Polene EVA MV1030 | TPI Polene Public Company Limited | EVA | Polene EVA |