Tecnoprene® AK7HCT NAT001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Tecnoprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IrGgnT_Tecnoprene-AK7HCT-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High crystallinity polypropylene homopolymer reinforced with 35% chemically coupled glass fiber, high heat stabilization |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.40 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Ash Content | 35 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 105 | MPa | ASTM D638 |
| Flexural Modulus | 8600 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 151 | °C | ASTM D648 |
| Vicat Softening Temperature | 139 | °C | ASTM D1525 1 |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant (1 kHz) | 2.60 | ASTM D150 | |
| Comparative Tracking Index | 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 6504 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| SPESIN® KP213G30SB3 | Kolon Plastics, Inc. | PBT | SPESIN® |
| Duron PEI 2200 | ProPolymers Inc. | PEI | Duron |
| HOPELEN L-270A | Lotte Chemical Corporation | PP Homopolymer | HOPELEN |
| Karina GREEN PVC COMPOUND -E 870-40/511-A-IS (C850) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |