The Honeywell R-Series PMP film is made from polymethylpentene. It provides more toughness and heat resistance than standard polyolefins for release film applications. R-Series Film is available in the following colors: Blue and Clear.

General Information
Features	Heat resistance, medium Good toughness
Uses	release film
Appearance	Blue Clear/transparent
Forms	Films

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.908	g/cm³	ASTM D792

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.55	ASTM D1894
With self-dynamics	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
secant modulus			ASTM D882
MD	665	MPa	ASTM D882
TD	707	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield	36.9	MPa	ASTM D882
TD : Fracture	30.3	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Fracture	250	%	ASTM D882
TD : Fracture	350	%	ASTM D882
Water Vapor Transmission	60	g/m²/24 hr	ASTM E96

Additional Information
Yield: 20339 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4000 to 6500 psiTensile Strength @ Break, ASTM D 882, TD: 3800 to 5000 psiElongation @ Break, ASTM 882, MD: 200 to 300%Elongation @ Break, ASTM 882, TD: 400 to 500%Secant Modulus, ASTM D 882, MD: 83000 to 110000 psiSecant Modulus, ASTM D 882, TD: 90000 to 115000 psiGraves Tear (initial), ASTM D 1004, MD: 275 to 325 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 300 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <2% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <1.5% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.4 to 0.7Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.8 to 1.2

Additional Information

Yield: 20339 in²/lbTensile Strength @ Yield, ASTM D 882, MD: 4000 to 6500 psiTensile Strength @ Break, ASTM D 882, TD: 3800 to 5000 psiElongation @ Break, ASTM 882, MD: 200 to 300%Elongation @ Break, ASTM 882, TD: 400 to 500%Secant Modulus, ASTM D 882, MD: 83000 to 110000 psiSecant Modulus, ASTM D 882, TD: 90000 to 115000 psiGraves Tear (initial), ASTM D 1004, MD: 275 to 325 g/milGraves Tear (initial), ASTM D 1004, TD: 250 to 300 g/milDimensional Stability, ASTM D1204, TD, 300°F, 10 min: <2% shrinkageDimensional Stability, ASTM D1204, MD, 300°F, 10 min: <1.5% shrinkageCoef of Friction, ASTM D1894, Vs Metal - Dynamic: 0.4 to 0.7Coef of Friction, ASTM D1894, Vs Itself - Dynamic: 0.8 to 1.2

Resin Grade	Manufacturer	Category	Trademark
STERalloy™ FDG 2781	Hapco Inc.	TP, Unspecified	STERalloy™ FDG
SURPASS® FPs117 Series	NOVA Chemicals	LLDPE	SURPASS®
ALTECH® PA66 A 2035/508 GF35	ALBIS PLASTIC GmbH	Nylon 66	ALTECH® PA66
Axiall PVC 18853	Axiall Corporation	PVC, Flexible	Axiall PVC
Geon™ Vinyl Flexible 90463	PolyOne Corporation	PVC, Flexible	Geon™ Vinyl Flexible