Zytel® FG151L NC010
| Category: | Nylon 612 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IogaXA_Zytel-FG151L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Polyamide 612 with Developed for Food Contact Applications |
| General Information | |
|---|---|
| Additive |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.4 | -- | % | |
| Flow | 1.3 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 3.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.3 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1700 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 62.0 | 54.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | 18 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 17 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2100 | 1440 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 3.0 | kJ/m² | |
| 23°C | 3.5 | 4.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | 40 kJ/m² | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 65.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 181 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.1E-4 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.6E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.8E-4 | -- | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G7 | Taro Plast S.p.A. | PET | TAROLOX |
| Aplax P0513GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Fainplast PVC RH 612 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Petrothene® NA340212 | LyondellBasell Industries | LDPE | Petrothene® |
| ALTECH® PC ECO 1000/521 IM UV | ALBIS PLASTIC GmbH | PC | ALTECH® PC |