LNP™ LUBRICOMP™ RN001S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IoUfaI_LNPLUBRICOMPRN001Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RN001S is a compound based on Nylon 66 resin containing MOS2. Added features of this material include: Internally Lubricated, Heat Stabilized. Also known as: LNP* LUBRICOMP* Compound R- HS Product reorder name: RN001S |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 | g/cm³ | ASTM D792 |
| -- | 1.17 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4140 | MPa | ASTM D638 |
| -- | 3910 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 84.1 | MPa | ASTM D638 |
| Yield | 69.0 | MPa | ISO 527-2 |
| Fracture | 84.1 | MPa | ASTM D638 |
| Fracture | 69.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.9 | % | ASTM D638 |
| Yield | 2.1 | % | ISO 527-2 |
| Fracture | 3.8 | % | ASTM D638 |
| Fracture | 42 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 3450 | MPa | ASTM D790 |
| -- | 3400 | MPa | ISO 178 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.75 | ASTM D3702 Modified | |
| With Self-Static | 0.55 | ASTM D3702 Modified | |
| Wear Factor - Washer | 103 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 2.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 54 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 2.30 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 231 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 223 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 76.7 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 301 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 1001 | Teknor Apex Company | PVC, Flexible | APEX® |
| Hostacom TKS708D | LyondellBasell Industries | TPO (POE) | Hostacom |
| Plexiglas® Diffuse V045-68193 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Plexiglas® |
| Sylvin 4200-68 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |