SABIC® PC PC1800R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | SABIC® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Io6xo2_SABICPCPC1800Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC1800R resin is a medium-high flow (MFR = 18 at 300°C/1.2kg), heat stabilized, polycarbonate product with mold release designed for use in the general purpose molding market. It is available exclusively at www.sabicpc.com |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | Internal method | ||
| -- 1 | 0.50 - 0.70 | % | Internal method |
| 3.20 mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption | |||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 120 | ASTM D785 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2350 | MPa | ASTM D638 |
| -- | 2350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 63.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | > 70 | % | ASTM D638 |
| Fracture | > 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2300 | MPa | ASTM D790 |
| -- 7 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D256 |
| -30°C 9 | 12 | kJ/m² | ISO 180/1A |
| 23°C 10 | 70 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | No Break | ASTM D4812, ISO 180/1U | |
| -30°C 11 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 65.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 12 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 13 | 124 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 141 | °C | ISO 306/B50, ASTM D1525 14 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow | |||
| -40 to 95°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| 23 to 80°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177, ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength (1.60 mm) | 27 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150, IEC 60250 | ||
| 60 Hz | 3.00 | ASTM D150, IEC 60250 | |
| 1 MHz | 3.00 | ASTM D150, IEC 60250 | |
| Dissipation Factor | ASTM D150, IEC 60250 | ||
| 60 Hz | 1.0E-3 | ASTM D150, IEC 60250 | |
| 1 MHz | 0.010 | ASTM D150, IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance (2540 µm) | 88.0 - 90.0 | % | ASTM D1003 |
| Haze (2540 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 50 mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 911 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| AXELERON™ GP 6314 BK CPD | The Dow Chemical Company | LLDPE | AXELERON™ |
| Cheng Yu 3276 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| DINALON® B3S25 | Grupo Repol | Nylon 6 | DINALON® |
| Lucent PC PC/ABS-0406 | Lucent Polymers, Inc. | PC+ABS | Lucent PC |