Order Products : sales@su-jiao.com
TRANSMARE® 35HT20-0.001
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Transmare Compounding B.V. |
| Trademark: | TRANSMARE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | In4GUr_TRANSMARE-35HT20-0-001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRANSMARE® 35HT20-0.001 is a 20% fine white talc filled polypropylene homopolymer. It combines a high stiffness with very good flow properties. Suitable for (light) coloring. This grade contains an anti static agent. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (4.00 mm) | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 4.00 mm | 35.0 | MPa | |
| Break, 4.00 mm | 22.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 4.00 mm | 4.4 | % | |
| Break, 4.00 mm | 12 | % | |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 55.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1A | ||
| -40°C | 1.0 | kJ/m² | |
| 23°C | 2.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1U | ||
| -40°C | 13 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.1 | kJ/m² | |
| 23°C | 2.2 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -40°C | 13 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 155 | °C | ISO 306/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 170 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 240 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 66 A12^F | Polykemi AB | Nylon 66 | SCANAMID 66 |
| UNITIKA Nylon 6 CX-2500 | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| NILAMID® A3 AL40 | Nilit Plastics | Nylon 66 | NILAMID® |
| Geon™ Vinyl Rigid Extrusion L7703 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Lupoy® HP5004HF | LG Chem Ltd. | PC+ABS | Lupoy® |