RheTech Polypropylene T40P100-774UVA
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ikihgu_RheTech-Polypropylene-T40P100-774UVA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Talc Reinforced, Polypropylene, UV Stabilized, JA6A Black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 72 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 27.6 | MPa | ASTM D638 |
| Flexural Modulus | 3620 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 27 | J/m | ASTM D256 |
| Dart Drop Impact | 0.904 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 79.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 210 - 238 | °C | |
| Middle Temperature | 216 - 243 | °C | |
| Front Temperature | 221 - 249 | °C | |
| Nozzle Temperature | 227 - 238 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 2.76 - 10.3 | MPa | |
| Holding Pressure | 2.07 - 8.27 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependentScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependent |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Norpex® PPE AX200 HI Flow | Custom Resins Group | PPE | Norpex® |
| Cevian® SAG20 | PlastxWorld Inc. | ABS | Cevian® |
| Elastocon® 2865PE | Elastocon TPE Technologies | TPE | Elastocon® |
| INEOS PP 540-CA13 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| INLUBE INX-TPU-05140 | Infinity LTL Engineered Compounds | TPU, Unspecified | INLUBE |