Order Products : sales@su-jiao.com
Durethan® BKV 130 DUS008 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IizB01_Durethan-BKV-130-DUS008-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 30 % glass fibers, injection molding, improved impact strength |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.70 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.20 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.30 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9300 | 5200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 155 | 95.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.5 | 7.5 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 8600 | 4700 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 240 | 135 | MPa | |
| 23°C 6 | 245 | 160 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 6.3 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI, GR, 14-090, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | 75 | kJ/m² | |
| 23°C | 90 | 90 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | < 10 | < 10 | kJ/m² | |
| 23°C | 12 | 20 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 70 | 70 | kJ/m² | |
| 23°C | 80 | 85 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 2.60 | -- | J | |
| 23°C | 4.00 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 750 | -- | N | |
| 23°C | 930 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 213 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 222 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.0E-4 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinylbond 96-1050-21 Black | Colorite Polymers | PVC, Flexible | Vinylbond |
| WELLAMID Nylon 6600 MRGV 25/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Alkathene® Ultra LDD204 | Qenos Pty Ltd | LLDPE | Alkathene® Ultra |
| Delrin® 327UVE RD402 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| For-Tec E OC6OAN (Series: AD/PAX/CR) | KRAIBURG TPE | TPE | For-Tec E |