GELOY™ CR7500 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IgXKxP_GELOYCR7500resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High heat ASA with optimum flow-impact balance. For Automotive applications and Automotive colors only. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 6.3 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 11 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 6.60 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1970 | MPa | ASTM D638 |
| -- | 2040 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 33.0 | MPa | ASTM D638 |
| Fracture | 35.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.6 | % | ASTM D638 |
| Yield | 3.3 | % | ISO 527-2/5 |
| Fracture 5 | 60 | % | ASTM D638 |
| Fracture | 19 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2170 | MPa | ASTM D790 |
| -- 7 | 2060 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 64.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 68.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 14 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 60 | J/m | ASTM D256 |
| 23°C | 400 | J/m | ASTM D256 |
| -30°C 10 | 6.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 15 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 30.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 12 | 88.0 | °C | ISO 75-2/Ae |
| 1.8 MPa, unannealed, 64.0mm span 13 | 89.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 14 |
| -- | 102 | °C | ISO 306/B50 |
| -- | 105 | °C | ISO 306/B120 |
| Ball Pressure Test 15(98°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 9.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 - 95.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 245 - 260 | °C | |
| Nozzle Temperature | 235 - 255 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 60.0 - 85.0 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa | |
| Screw Speed | 30 - 80 | rpm | |
| Vent Depth | 0.038 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 80*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| 15 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILITE AC3800 | Formosa Plastics Corporation | PC | TAIRILITE |
| alphalon™ E 40 LN | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Clearflex® H&T FGH 196 | Versalis S.p.A. | LLDPE | Clearflex® H&T |
| Karina BLACK PVC COMPOUND -E 600-48/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PD1002NT | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |