Karina WHITE PVC COMPOUND 806-10/ 236-H-ISE
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IdhPy4_Karina-WHITE-PVC-COMPOUND-806-10-236-H-ISE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Karina WHITE PVC COMPOUND 806-10/ 236-H-ISE is a Polyvinyl Chloride product. It is available in Latin America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.47 to 1.53 | g/cm³ | ASTM D792 |
| Color | OK | ME 12 | |
| Color a | -1.57 to 0.430 | ME 12 | |
| Color b | -2.19 to -0.190 | ME 12 | |
| Color L | 90.2 to 92.2 | ME 12 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 10.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 200 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 10.0 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 200 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B1 GF 20 000/2 | Plastcom | PBT | SLOVASTER® |
| CP PRYME® Polycarbonate PC100RULUV-10M BT Clear | Chase Plastics Services Inc. | PC | CP PRYME® Polycarbonate |
| DESLON™ 66 DSC204GMH8 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Grilon® CR 9 HV | EMS-GRIVORY | Nylon 6/12 | Grilon® |
| LNP™ LUBRICOMP™ WFL369 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |