Maxxam™ FR PP301 SHI NC196
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ FR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IdXhQG_Maxxam-FR-PP301-SHI-NC196.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP, flame retardant |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792 |
| Molding Shrinkage | 1.2 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 25.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 150 | % | ASTM D638 |
| Flexural Modulus 3 | 1300 | MPa | ASTM D790 |
| Flexural Strength 4 | 38.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 100 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 90.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP5015 | PolyMirae | PP Impact Copolymer | Moplen |
| Axiall PVC 9017 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Cheng Yu ML3430 | Cheng Yu Plastic Company Limited | PC | Cheng Yu |
| Geon™ Vinyl Flexible D6500 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| OxyVinyls® 195F | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |