MAJORIS CT200
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Id3RLz_MAJORIS-CT200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CT200 is a 20% mineral filled grade intended for injection moulding. The product is available in black (CT200 - 8229) but other colours can be supplied on request. CT200 has been developed especially for the car industry, to be used in interior parts and also an excellent balance between the impact strength and stiffness, and it has very good surface quality. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 230°C/2.16 kg | 6.5 | g/10 min | ISO 1133 |
| 230°C/5.0 kg | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.6 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 31.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 2250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 61.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A |
| -- | 80.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 60% of injection pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermec™ 4150R40 | Technical Polymers, LLC | PPS | Thermec™ |
| Vi-Chem PVC V143-70E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| NORYL GTX™ GTX918W resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| BFI 428 | Blueridge Films Inc. | HDPE | BFI |
| EMERGE™ PC 8230-31 | Trinseo | PC | EMERGE™ |