Ferro PP TPP40AC38WH
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | IcOltV_Ferro-PP-TPP40AC38WH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Meets/Exceeds Ford Engineering Specification WSK-M4D644-A4. Primary end use is for instrument clusters. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.32 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 5.7 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 5.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 1.0 | % | ASTM D955 |
| -- | 1.3 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 29.0 | MPa | ASTM D638 |
| Yield, 23°C | 27.6 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 11 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2900 | MPa | ASTM D790 |
| -- | 3800 | MPa | ISO 178 |
| Flexural Strength (Yield) | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| -40°C | 1.7 | kJ/m² | ISO 180 |
| 23°C | 2.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C) | 270 | J/m | ASTM D256 |
| Dart Drop Impact | 1.02 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 129 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 82.2 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 82.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tensile/Izod Change, ISO 188, 2000 hours, 150°C: +11%/-8% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 204 - 210 | °C | |
| Middle Temperature | 210 - 213 | °C | |
| Front Temperature | 213 - 216 | °C | |
| Nozzle Temperature | 216 - 218 | °C | |
| Mold Temperature | 43.3 - 54.4 | °C | |
| Back Pressure | 0.138 - 0.345 | MPa | |
| Screw Speed | 100 - 150 | rpm | |
| Clamp Tonnage | 2.8 - 4.1 | kN/cm² | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ad-Tech Epoxy EC-418 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Axiall PVC 7777 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| KumhoSunny PC HCG2530MP | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| Kumho KNB 1845 | Korea Kumho Petrochemical Co., Ltd. | NBR | Kumho KNB |
| Vydyne® R530H BK0713 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |